SP2-1000 is a pattern wax that does not include a filler material. Therefore, the wax pattern surface is thin and smooth. Additionally, there is no mold cracking through de-waxing because the viscosity of the wax in its liquid state is very low.This wax is suitable for the production of the high quality investment casting products such as turbine blades and nuclear power generation parts.
Physical Properties (Representative Value)
| Wax Type |
Non-Filled Wax |
| Color |
Green |
| Softening point |
68ﾟC |
| Congealing Point |
55ﾟC |
| Needle Penetration 200g/5sec./25ﾟC |
10 |
| Viscosity |
120ﾟC |
33 mPa·s |
| 110ﾟC |
45 mPa·s |
| 100ﾟC |
69 mPa·s |
Contraction by Injection Test Piece (Representative Value)
| Injection Test Parameter |
Injection Temperature |
54ﾟC |
| Injection Pressure |
30 kg/cm2 |
| Injection time |
20 sec. |
| Contraction |
125 mm |
0.85% |
| 75 mm |
0.79% |
| Surface Sink |
0.23 mm |
| Length of Wax Flow |
161 mm |
Strength by 3 Points Bending Test (Representative Value)
| Size of Test Bar |
10×10×80 mm |
| Span |
60 mm |
| Maximum Load |
55 N |
| Maximum Bending Stress at Maximum Load |
5.0 MPa |
| Maximum Bending Strain at Maximum Load |
3.7 mm |
| Young's Modulus |
346 MPa |